Home > Products Information > Polyolefin Heat Shrink Tubing |
|
|
| |
Polyolefin Heat Shrink Tubing |
|
|
|
|
|
 |
Products Infomation:
●Shrink Ratio;2:1、3：1
●Operating Temperature Range-55℃to135℃
●Shrink Temperature 120℃
●Resistance to aviation and diesel fuels makes it suitable for protecting military ground cables and harnesses
Standard Colours:
Black
Products Characters:
| PROPERTY |
Test Method |
Standard Repuired |
| Tensile |
ASTM D638 |
≥10.4MPa |
| Elongation |
ASTM D638 |
≥200% |
| Electric Strength |
ASTM D150 |
≥15KV/mm |
| volume Resistivity |
ASTM D876 |
≥1014Ω.cm |
| Water Absorption |
ASTM D570 |
≤0.5% |
| Copper stability |
UL 224 |
PASS |
Standard Size(2:1) :
| Size |
Inside diameter(mm) |
After Recovery |
Package(M/Roll) |
| (mm) Inside diameter(Max) |
Wall-thickness |
|
| Φ0.8 |
1.2 |
0.6 |
0.1±0.01 |
200 |
| Φ1.0 |
1.6 |
0.8 |
0.1±0.01 |
200 |
| Φ2.0 |
2.4 |
1.2 |
0.1±0.01 |
200 |
| Φ3.0 |
3.2 |
1.6 |
0.2±0.01 |
200 |
| Φ4.5 |
4.8 |
2.4 |
0.23±0.02 |
100 |
| Φ6.0 |
6.4 |
3.2 |
0.28±0.02 |
100 |
| Φ9.0 |
9.5 |
4.8 |
0.3±0.02 |
100 |
| Φ12 |
12.7 |
6.4 |
0.3±0.02 |
50 |
| Φ16 |
16.0 |
8.0 |
0.38±0.08 |
50 |
| Φ18 |
19.1 |
9.5 |
0.38±0.08 |
50 |
| Φ25 |
25.4 |
12.7 |
0.45±0.15 |
50 |
| Φ40 |
38.1 |
19.1 |
0.5±0.15 |
50 |
| Φ50 |
50.8 |
25.4 |
0.5±0.15 |
25 |
| Φ80 |
76.2 |
38.1 |
0.75±0.15 |
25 |
| Φ100 |
101.6 |
50.8 |
0.8±0.2 |
25 |
Standard Size(3:1) :
| Size |
Inside diameter (mm) |
After Recovery |
Package(M/Roll) |
| (mm) Inside diameter(Max) |
Wall-thickness |
|
| Φ3.2 |
> 3.2 |
> 1.0 |
0.65±0.10 |
200 |
| Φ4.5 |
> 4.5 |
> 1.5 |
0.65±0.10 |
100 |
| Φ6.0 |
> 6.0 |
> 2.0 |
0.75±0.10 |
100 |
| Φ9.0 |
> 9.0 |
> 3.0 |
0.95±0.15 |
50 |
| Φ12.0 |
> 12.0 |
> 4.0 |
1.10±0.15 |
50 |
| Φ15.0 |
> 15.0 |
> 5.0 |
1.15±0.15 |
50 |
| Φ18.0 |
> 18.0 |
> 6.0 |
1.25±0.15 |
50 |
| Φ24.0 |
> 24.0 |
> 8.0 |
1.50±0.20 |
25 |
| Φ30.0 |
> 30.0 |
> 10.0 |
1.70±0.20 |
1.22 |
| Φ39.0 |
> 39.0 |
> 13.0 |
1.90±0.20 |
1.22 |
| Φ50.0 |
> 50.0 |
> 16.0 |
2.50±0.20 |
1 |
| Φ60.0 |
> 60.0 |
> 20.0 |
2.60±0.20 |
1 |
|
| |
|